Tali Sili Silicon Carbide Malosi Maualuga Maualuga Sa'o Sisic/ Rbsic Rollers ma Beams
O le tali sintering silicon carbide ceramics roller e masani ona faʻaaogaina mo le gaosiga o le maa lithium, porcelain i aso taʻitasi, porcelain sanitary, fau fale ma mea faʻamaneta, e pei o le kiln roller, maualuga vevela mu ma lelei kiln, ma se olaga umi auaunaga. E i ai le malosi maualuga o le vevela, faʻalavelave faʻafuaseʻi vevela, maualuga le vevela o le fetolofi, malosi malosi, lelei le ofuina. i lua – fa'aa'amea fa'a'ugāumu ma isi uta ogaumu fa'apisinisi - fa'atulagaina fa'avaa.
O kalapu e fa'aoga i aso ta'itasi – sima fa'aoga, porcelain tumama, Keramik Faufale, Mea fa'amaneta ma sone fa'avevela o le umu uila.
| Silicon Carbide Fa'amatalaga o oloa: | ||||
| Aitema | Vaega | SSIC | RBSIC SISIC | R-SIC |
| Mama | ( %) | ≥ 99 | ≥90% | ≥ 99 |
| Fa'aoga vevela | ºC | 1700 | 1380 | 1650 |
| Malosi | g/CM2 | ≥3.10-3.15 | ≥3.02 | 2.65-2.75 |
| Matala porosity | % | ≤0.1 | ≤0.1 | |
| Malosi | ≥92 HRA | 2400 Kilokalama/mm2 | 1800-2000 Kg/mm2 | |
| Malosi punou | MPa | 400-580 | 250(20ºC) | ≥300 |
| 281(1200ºC) | ||||
| Malosi fa'asa | Mpa | ≥200 | ≥190 | |
| modulus o elasticity | GPa | 400 | 332(20ºC) | 80-100(20ºC) |
| 300(1200ºC) | 90-110(1200ºC) | |||
| Amioga vevela | W/mk | 100-120 | 45(1200ºC) | 36 |
| Coefficient o le faalauteleina o le vevela | K1X 106 | 4.2 | 4.5 | 4.6 |
| Malosi | Gpa | >25 | 13 | |
| Acid & Ikali tetee | Lelei | Lelei | Lelei | |
| SiC Oloa Fa'amatalaga: | ||||
| Aitema | Vaega | OC-1 | OC-2 | MC-3 |
| SiC | (%) | ≥90 | ≥86 | ≥80 |
| E aliali mai Porosity | (%) | ≤10 | ≤13 | ≤16 |
| Malosi | g/CM2 | ≥2.66 | ≥2.63 | ≥2.6 |
| Fa'aoga vevela | ºC | ≥1680 | ≥1620 | ≥1550 |
| Coefficient o le faalauteleina o le vevela | aX 10-6/ºC | ≤4.8 | ≤5.0 | ≤5.5 |
| Malosi punou | 1200ºC | ≥45 | ≥40 | ≥30 |
Shandong Zhongpeng Special Ceramics Co., Ltd o se tasi o silicon carbide ceramic fofo fou meafaitino i Saina. SiC fa'atekinisi sima: O le maaa o Moh e 9 (New Moh's ma'a'a e 13), fa'atasi ai ma le lelei tele o le tete'e atu i le tafia ma le a'a, sili ona lelei abrasion - tete'e ma le fa'ama'i fa'ama'i. O le ola tautua a le SiC e 4 i le 5 taimi umi atu nai lo le 92% mea alumina. O le MOR o le RBSiC e 5 i le 7 taimi o le SNBSC, e mafai ona faʻaoga mo foliga sili atu ona faigata. O le faiga o upusii e vave, o le tuʻuina atu e pei ona folafolaina ma o le lelei e le lua. Matou te faʻaauau pea i le luʻiina o matou sini ma toe tuʻuina atu o matou loto i le sosaiete.