Silicon carbide beams and rollers for kiln
Reaction Bonded Silicon Carbide High Strength High Straightness Sisic/ Rbsic Rollers and Beams
Reaction sintering silicon carbide ceramics roller is mainly used for lithium battery industry, daily porcelain, sanitary porcelain, building ceramics and magnetic materials, such as roller kiln, high temperature burning with ideal kiln, with a long service life. It has high temperature strength, thermal shock resistance, high temperature creep resistance, strong resistance, good wear resistance.. Rollers with high – temperature bearing capacity of large, long-term use without bending deformation, especially suitable for tunnel kilns, shuttle kiln, in two – layer roller kiln and other industrial furnace load – bearing structure of frame.
Clubs apply to daily – used ceramics, sanitary porcelain, Building Ceramic, Magnetic material and high temperature firing zone of roller kiln.
| Silicon Carbide Product Specification: | ||||
| Item | Unit | SSIC | RBSIC SISIC | R-SIC |
| Purity | ( % ) | ≥ 99 | ≥90% | ≥ 99 |
| Application temperature | ºC | 1700 | 1380 | 1650 |
| Density | g/CM2 | ≥3.10-3.15 | ≥3.02 | 2.65-2.75 |
| Open porosity | % | ≤0.1 | ≤0.1 | |
| Hardness | ≥92 HRA | 2400 Kg/mm2 | 1800-2000 Kg/mm2 | |
| Bending strength | MPa | 400-580 | 250(20ºC) | ≥300 |
| 281(1200ºC) | ||||
| Tensile strength | Mpa | ≥200 | ≥190 | |
| modulus of elasticity | GPa | 400 | 332(20ºC) | 80-100(20ºC) |
| 300(1200ºC) | 90-110(1200ºC) | |||
| Thermal Conductivity | W/m.k | 100-120 | 45(1200ºC) | 36 |
| Coefficient of thermal expansion | K1X 106 | 4.2 | 4.5 | 4.6 |
| Rigidity | Gpa | >25 | 13 | |
| Acid&Ikali resistance | Excellent | Excellent | Excellent | |
| SiC Product Specification: | ||||
| Item | Unit | OC-1 | OC-2 | MC-3 |
| SiC | (%) | ≥90 | ≥86 | ≥80 |
| Apparent Porosity | (%) | ≤10 | ≤13 | ≤16 |
| Density | g/CM2 | ≥2.66 | ≥2.63 | ≥2.6 |
| Application temperature | ºC | ≥1680 | ≥1620 | ≥1550 |
| Coefficient of thermal expansion | aX 10-6/ºC | ≤4.8 | ≤5.0 | ≤5.5 |
| Bending Strength | 1200ºC | ≥45 | ≥40 | ≥30 |
Shandong Zhongpeng Special Ceramics Co., Ltd is one of the largest silicon carbide ceramic new material solutions in China. SiC technical ceramic: Moh’s hardness is 9 (New Moh’s hardness is 13), with excellent resistance to erosion and corrosion, excellent abrasion – resistance and anti-oxidation. SiC product’s service life is 4 to 5 times longer than 92% alumina material. The MOR of RBSiC is 5 to 7 times that of SNBSC, it can be used for more complex shapes. The quotation process is quick, the delivery is as promised and the quality is second to none. We always persist in challenging our goals and give our hearts back to society.