SCSC - Th yabaye ibikoresho birwanya kwambara kwambara kubyara ibiyiko bya hydrocyclone.
Imitungo ya Clicon Carbide Ibicuruzwa byananiranye birimo gukomera gukomeye, imbaraga nyinshi no kurambura cyane. Ariko, ibicuruzwa nkibi bifite ibibi, nko gutonesha, guhagarika nibindi. Kugirango uhuze n'imikorere ya hydrocyclone, igomba gukomeza kurushaho. Zhongpeng yateje imbere inzira yacyo, yateye imbere kandi igatangiza ibintu bishya byambarwa bikwiranye na Cyclone nyinshi bita no kurwanya SCSC - th. Nibintu bishya bya kristalline wongeyeho ibimenyetso mubintu mugice cya silicon carbide no kurira no gukira no kwishyurwa cyane. Ibigize imiti minini yimiti ni sic, c, mo, etc. binary cyangwa byinshi imiterere yububiko bwa hexagonal ikorwa mubushyuhe bwo hejuru. Kubwibyo, iki gicuruzwa gifite ubukana buhebuje, imbaraga nyinshi, kwihitiramo (guterana amagambo), kurwanya anti-anti-anti-anti-ihohoterwa hamwe no kurwanya ubushyuhe bwinshi.
Ibigize imiti hamwe nimitungo yumubiri irerekanwa mu mbonerahamwe ya 1 nameza 2.
Imbonerahamwe 1: Ibigize imiti
| Amabuye y'agaciro | Silicon Carbide Ceramics | Nitrous oxide | Silicon yubusa |
| ɑ - sic | ≥98% | ≤0. 3% | ≤0. 5% |
Imbonerahamwe 2: Ibintu byumubiri
| Ibintu | Umunyabyaha wa Silicon Silicon mukibazo cyikirere | Reaction yubusa nyabagendwa silicon carbide |
| Ubucucike | 3. 1 G / CM3 | 3. 02 G / CM3 |
| Porositity | <0. 1% | <0. 1% |
| Kunama imbaraga | 400 MPA | 280 mpa |
| Elastike modulus | 420 | 300 |
| Acide na Alkali Kurwanya Alkali | Byiza | Byiza |
| Abagore-Gukomera | 18 | 22 |
| Abrasion | ≤0. 15 | ≤0. 01 |
Mubihe bimwe, kugereranya imitungo hagati ya SCS - th na alumina ceramics yerekanwe mu mbonerahamwe ya 3.
Imbonerahamwe 3: Kugereranya imitungo hagati ya SCS - th na Ai2O3
| Ibintu | Ubucucike (g * cm3) | Igipimo gikomeye | Microhardness (kg * mm2) | Kunama imbaraga (MPA) | Abrasion |
| Ai2O3 | 3.6 | 7 | 2800 | 200 | ≤0. 15 |
| SCSC - TH | 3.02 | 9.3 | 3400 | 280 | ≤0. 01 |
Ubuzima bwa serivisi ya sisitemu yo hagati ya sisitemu yo hagati hamwe no gushyigikira umuyoboro urwanya wambara wakozwe na SCSC - TH ni inshuro 3 ~ 5 iyeho2O3 Kandi inshuro zirenga 10 zo kwambara. Umurongo wakozwe na SCSC - th urashobora kongera ukugarura amakara meza kurenza 1%. Serivisi Ubuzima Bugereranya Ai2O3 na SCSC - TH ni izi zikurikira:
Imbonerahamwe 4: Kugereranya bivamo ingaruka zo gutandukana ziterwa ninkubi y'umuyaga idasanzwe (%)
| Ibintu | Ibirimo <1. 5 | Ibirimo 1.5 ~ 1. 8 | Ibirimo> 1.8 |
| Ai2O3 liner | SCSC - LINER | Ai2O3 liner | SCSC - LINER | Ai2O3 liner | SCSC - LINER |
| Amakara meza | 93 | 94.5 | 7 | 5.5 | 0 | 0 |
| Ububiko | 15 | 11 | 73 | 77 | 12 | 8 |
| Imyanda | | | 1.9 | 1.1 | 98.1 | 98.9 |
Imbonerahamwe 5: Ubuzima Bwa serivisi Kugereranya Ai2O3 na SCSC
| | Ai2O3 Spigot | Scsc - spigot |
| Gupima kuri abrasion | 300 d | 120 D Guhana | Abrasion hamwe na 1.5mm nubuzima bwa serivisi hejuru ya 3a |
| 500 D. | Abrasion hamwe na 2mm nubuzima bwa serivisi hejuru ya 3a |
| Ikiguzi cyo gufata neza | 300 d | 200.000 | 0 |
| 500 D. | 300.000 | 0 |