ZPC-RSSIC (Sisic) Obe osisi na rollers nwere ike dị elu ma enweghị mmezi ọbụla na okpomọkụ dị oke elu. Ọzọkwa na-egosipụta ogologo ndụ ọrụ. Osisi ndị ahụ bụ nnukwu ụlọ na-eme ka mma maka iyi dị ọcha na ngwa ebe a na-ere eletrik. RSns (Sisic) nwere ezigbo ihe na-akpata, yabụ ọ dịla ka ịchekwaa ike na obere ibu nke Kiln ụgbọ ala.
A na-eji osisi silicon carbide na-emepụta kilomita, nke nwere ike iji okpokolo agba dị ka ha nwere ezigbo ọrụ, na oge ndụ a bụ ezigbo arịa ụlọ. A na-ejikarị osisi silicon carbide mee ihe dị ka ibu ibu nke Kinnel Kiln, mechie zil na ọwa abụọ. Enwere ike iji ya dị ka arịa ụlọ na seramiiki na ụlọ ọrụ recreatic.
Ihu igwe nwere ike - ike ikuku nke buru ibu, ogologo iji na-enweghị nrụrụ, nke dị mma maka ọwara Kination Kiln, na-ebugharị roller kilogram - na-egbu nke etiti. Klọb na-emetụta kwa ụbọchị - eji caramis, nke na-ewu ewu, na-ewu seramic, ihe ndọta na mpaghara ọkụ dị elu nke roller Kilo.
| Ihe | Rbs (Sisic) | Sogi | |
|---|---|---|---|
| Unit | Data | Data | |
| Max nke oge okpomọkụ nke akwụkwọ | C | 1380 | 1600 |
| Keuju | g / cm3 | > 3.02 | > 3.1 |
| Mepere polonity | % | <0.1 | <0.1 |
| Ike | Anamba | 250 (20c) | > 400 |
| Anamba | 280 (1200 c) | ||
| Modulu nke adiamac | Gpa | 330 (20C) | 420 |
| Gpa | 300 (1200c) | ||
| Ọkụ na-eme ihe ọkụkụ | W / mk | 45 (1200 c) | 74 |
| Coefficitation nke mgbasa ikuku | K x 10 | 4.5 | 4.1 |
| HV siri ike | Gpa | 20 | 22 |
| Acid alkaline - proff |
Njirimara:
* Iguzogide elu
* Arụmọrụ ike dị elu
* Ọ dịghị nrụrụ n'okpuru okpomọkụ dị elu
* Oke ndidi okpomoku nke 1380-1650 Celsius
* Na-eguzogide
* Ike dị elu na-agbada n'okpuru ogo 1100: 100-120MPA
Shandonng Zhongpen Coramics Coramis Coramic Coramic Coramic Coramic Coramic. Telitic Ser Par: Ndụ Sec ngwaahịa dị afọ 4 ruo ugboro ise karịa 92% alumina. Na mor nke rbssic bụ ugboro ise nke snikc, enwere ike iji ya mee ihe ndị ọzọ mgbagwoju anya. Usoro e kwuru okwu ya bụ ngwa ngwa, nnyefe ahụ dị ka ekwere na ogo bụ nke abụọ ọ bụla. Anyị na-anọgidesi ike mgbe niile n'inweta ihe mgbaru ọsọ anyị ma nye anyị obi.