ʻO nā kaola silikoni carbide a me nā wili no ke kiln
Reaction Bonded Silicon Carbide kiʻekiʻe kiʻekiʻe Straightness kiʻekiʻe Sisic/ Rbsic Rollers a me nā kaola
Hoʻohana nui ʻia ʻo Reaction sintering silicon carbide ceramics roller no ka ʻoihana pākaukau lithium, porcelain i kēlā me kēia lā, porcelain sanitary, kūkulu hale a me nā mea magnetic, e like me ka roller kiln, ke ahi wela kiʻekiʻe me ka kiln maikaʻi, me ke ola lōʻihi. Loaʻa iā ia ka ikaika wela kiʻekiʻe, ke kū ʻana o ka haʻalulu wela, ke kūpaʻa kiʻekiʻe o ke kolo, ke kūpaʻa ikaika, ke kūpaʻa maikaʻi.
Hoʻohana ʻia nā hui i kēlā me kēia lā - nā seramika i hoʻohana ʻia, porcelain maʻemaʻe, Building Ceramic, Material Magnetic a me kahi kiʻekiʻe kiʻekiʻe kiʻi ahi o ka roller kiln.
| Hua'ōlelo Hua'ōlelo Silicon Carbide: | ||||
| 'ikamu | Unite | SSIC | RBSIC SISIC | R-SIC |
| Maemae | (%) | ≥ 99 | ≥90% | ≥ 99 |
| Ka wela noi | ºC | 1700 | 1380 | 1650 |
| ʻO ka mānoanoa | g/CM2 | ≥3.10-3.15 | ≥3.02 | 2.65-2.75 |
| ʻO ka porosity wehe | % | ≤0.1 | ≤0.1 | |
| ʻoʻoleʻa | ≥92 HRA | 2400 Kg/mm2 | 1800-2000 Kg/mm2 | |
| Ka ikaika kulou | MPa | 400-580 | 250(20ºC) | ≥300 |
| 281(1200ºC) | ||||
| Ka ikaika tensile | Mpa | ≥200 | ≥190 | |
| modulus o ka elasticity | GPa | 400 | 332(20ºC) | 80-100(20ºC) |
| 300(1200ºC) | 90-110(1200ºC) | |||
| ʻO ka hoʻoili wela | W/mk | 100-120 | 45(1200ºC) | 36 |
| Coefficient o ka hoonui wela | K1X 106 | 4.2 | 4.5 | 4.6 |
| ʻoʻoleʻa | Gpa | >25 | 13 | |
| Acid&Ikali resistance | Maikaʻi | Maikaʻi | Maikaʻi | |
| Hōʻike huahana SiC: | ||||
| 'ikamu | Unite | OC-1 | OC-2 | MC-3 |
| SiC | (%) | ≥90 | ≥86 | ≥80 |
| ʻIke ʻia ka Porosity | (%) | ≤10 | ≤13 | ≤16 |
| ʻO ka mānoanoa | g/CM2 | ≥2.66 | ≥2.63 | ≥2.6 |
| Ka wela noi | ºC | ≥1680 | ≥1620 | ≥1550 |
| Coefficient o ka hoonui wela | aX 10-6/ºC | ≤4.8 | ≤5.0 | ≤5.5 |
| Kulou ikaika | 1200ºC | ≥45 | ≥40 | ≥30 |
ʻO Shandong Zhongpeng Special Ceramics Co., Ltd ʻo ia kekahi o ka silicon carbide ceramic mea hoʻonā hou i Kina. ʻO ka ʻenehana loea SiC: ʻO 9 ka paʻakikī o Moh (ʻo 13 ka paʻakikī o New Moh), me ke kūpaʻa maikaʻi loa i ka erosion a me ka corrosion, abrasion maikaʻi loa - kūpaʻa a me ka anti-oxidation. ʻO ke ola lawelawe o ka huahana SiC he 4 a 5 mau manawa lōʻihi ma mua o 92% alumina mea. ʻO ka MOR o RBSiC he 5 a 7 mau manawa o ka SNBSC, hiki ke hoʻohana ʻia no nā ʻano paʻakikī. He wikiwiki ke kaʻina hana, ʻo ka hāʻawi ʻana e like me ka mea i ʻōlelo ʻia a ʻoi aku ka maikaʻi o ka lua. Ke hoʻomau mau nei mākou i ka hoʻokūkū i kā mākou mau pahuhopu a hāʻawi i ko mākou naʻau i ke kaiāulu.